Narrow Neck Erlenmeyer Flask

Erlenmeyer flask. Borosilicate glass LGB 3.3. Graduated. According to DIN 12380, ISO
1773. Sterilisable in autoclave at 121º. In different volumes, 50ml, 100ml, 250ml, 500ml and 1000ml.

FLASKS: TECHNICAL PROPERTIES

MATRAZ ERLENMEYER DE BOROSILICATO

Borosilicate glass 3.3 is a glass with minimal silica content.
It is practically free of magnesium, lime and zinc and contains only traces of heavy metals.

Chemical composition:

• 81% by weight SiO2
• 13,0% by weight of B2O3
• 4% by weight of Na2O

Thermal properties:
Coefficient of linear expansion: 32,5 x10-7 º C
Maximum working temperature : 515 º C
Annealing temperature: 565 º C
Softening temperature: 820 º C
Specific heat: 0,2
Thermal conductivity (cal/cm3 / º C / sec): 0.0027
Chemical Resistance:
Este vidrio es altamente resistente al agua, soluciones neutras y ácidas, ácidos concentrados y sus mezclas, así como a cloruro, bromo, yodo, y disolventes orgánicos. Incluso durante el largos períodos de exposición y a temperaturas superiores a 100 ° C, su resistencia química supera la de la mayoría de los metales y otros materiales.
It can withstand repeated dry and wet sterilisation without surface deterioration and consequent
contaminación. Resiste al ataque de diversas sustancias químicas. Sólo el ácido fluorhídrico, el ácido fosfórico muy caliente y soluciones alcalinas con el aumento de la concentración y la temperatura, atacan cada vez más la superficie de vidrio.